Curing Agent for Rubber Accelerator
DPOCURE
MBT & MBTS

Product Application
Accelerator choice is critical. Selecting a good accelerator system is difficult. Many parameters, such as raw rubber storage stability, processability, scorch, crosslinking, and cured rubber requirements to name a few, come into consideration. Primary accelerators such as DPL DPOCURE MBT and MBTS are the most popular accelerators and offer a good start. Their good qualities are the effective acceleration they provide at medium and high temperatures and their wide range of curing rates and scorching characteristics. They usually provide considerable scorch delay, medium to fast cure, and good modulus development.
Heat Insulation Industry
MBT & MBTS Curing Agent
EVA Sheet Industry
MBT & MBTS Curing Agent

Heat Insulation Industry
MBT & MBTS Curing Agent

EVA Sheet Industry
MBT & MBTS Curing Agent
Plastic Industry
MBT & MBTS Curing Agent
Rubber industry
MBT & MBTS Curing Agent

Plastic Industry
MBT & MBTS Curing Agent

Rubber industry
MBT & MBTS Curing Agent
PRODUCT SPECIFICATIONS
Property | Standard | Result 1 | Result 2 |
---|---|---|---|
APPEARANCE | FAINT YELLOW POWDER | Similar | Similar |
ASH (%) ≤ | 0.8 | 0.05 | 0.17 |
DECOMPOSITION TEMPERATURE (°C) | 200-210 | 204.0 | 203.3 |
PURITY (%) ≥ | 97 | 98.6 | 97.6 |
GAS-FORMING AMOUNT (ML/G) ≥ | 220 | 235 | 7.5 |
AVERAGE DIAMETER OF GRANULA ≤ (UM) | 16~18 | 0.09 | 0.10 |
LOSS ON HEATING (%) ≤ | 0.3 | 0.0035 | 0.02 |
RESIDUAL ON SIEVE (%)≤ | 0.2 |